YBS-LPA01

Characteristics & description

YBS-LPA01 is a saturated resin as a low profile additive. the resin can control the shrinkage of the product, improve the surface quality of the product, and has a wide range of process applicability, especially suitable for the SMC、BMC molding process.

BMC Initial Formulation
Ingredientweight/kg
Molding Resin60
Low Shrinkage Agent40
TBPB1.5
Zinc Stearate4
CaCO3150
MgO paste (35% MgO content)2.5


Liquid index of resin:

Product name Acid value(mg.KOH/g) Viscosity(25℃ pa.s) Gel Time(25℃,min) Non-Volatile(%)
YBS-LPA01 3.0-6.5 0.14-0.18 39.0-43.0

Performance index of castable body:

Product name Tensile Strength(Mpa) Breaking Elongation(%) Bending Strength(Mpa) Bending modulus(Gpa)
Distortion Temperature(℃) Barcol hardness
YBS-LPA01

Product Application:

YBS-LPA01 resin is a low shrinkage agent in BMC/SMC.

Storage & Use:

1、Before use, the resin should be in the original packaging (avoid breakage of the barrel and barrel),25℃ below the dry indoor storage period of three months. Keep the barrel sealed to prevent moisture from invading and tighten the lid.

2、The increase of temperature and light exposure will significantly shorten the storage period, storage should be away from heat sources and avoid direct sunlight.

3、Unsaturated polyester resin containing styrene is flammable and stored away from open fire.

4、If the resin is not used properly, it will cause injury. Avoid contact with skin and eyes. Wear necessary protective equipment and clothing. For product safety instructions, see Yibeisen's "resin safety instructions (MSDS)"

Attention:

This information is based on the type index formulated according to the GB standard. due to the development, improvement and revision of the product technology, the physical product may not conform to this product specification. It is recommended that users need to test and test before use. The Company reserves the right to modify certain technical parameters.


-->